Suitable for jewelry industry, dental, clock, glasses, teaching and scientific research, toy design, handicraft design, industrial parts design, etc
 
Product Advantages:
Short curing time, fine surface, finest detail features.
After curing, the printed piece has high hardness and toughness.
 
Product Technical Parameters before Curing
Viscosity: 300~500mPa·s (NDJ-8S rotary rheometer（25℃）)
Density: 1.05~1.25g/cm3 (densitometer(25℃))
 
Recommended Print Parameters
Recommended printing time: Bottom exposure time 20-30s, layer exposure time 2.5s-3s. (based on the printer with intensity of 3500-4500µw/㎝²)
Bottom Lift Distance: 6mm
Lifting Distance: 6mm
Bottom Lift Speed: 60mm/min
Lifting Speed: 80mm/min
Retract Speed: 150mm/min
Wavelength: 385~410nm
 
Molding Test Requirements and Technical Parameters after Molding     
Molding Test Environment and Standard:
①Temperature: 23±2℃
②Relative humidity: 50%RH±5%RH
③The standard of the test piece: ASTM
④Post curing condition: The test piece was placed in water under 405nm ultraviolet radiation of 200mw/cm² for one minute.
Technical Parameters after Molding:
Maximum force(KGF): 168.7±10%
Tensile strength(MPa): 45.62±10%
Deformation of maximum point of force(mm): 5.75±10%
Elongation at yield point(%): 6.34±10%
Elongation at break(%): 11.5±10%
Maximum bending strength(MPa): 58.3±10%
Flexural modulus(MPa): 1123.2±10%
Hardness(Shore D)：80-85
Impact strength(j/m): 76±10%
Tensile modulus：608.5±10%